PPS HAVE
1Excellent chemical resistance
2tight tolerance
3better thermal performance
4dimensional stable flame retardant
Property | Test Method | Units | Fiberglass Reinforced | |||||
P130T | P130T-04 | P140T | P140T-02 | P140T-04 | ||||
Physical | Density | ISO 1183 | g/cm3 | 1.56 | 1.56 | 1.65 | 1.65 | 1.65 |
Water Absorption | ISO 62 | % | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | |
MD/TD* | - | % | 0.4/0.7 | 0.4/0.7 | 0.3/0.6 | 0.3/0.6 | 0.3/0.6 | |
Mechanical | Tensile Strength | ISO 527 | MPa | 150 | 145 | 185 | 180 | 175 |
Elongation at Break | ISO 527 | % | 3.0 | 6.0 | 2.0 | 4.0 | 4.0 | |
Flexural Strength | ISO 178 | MPa | 220 | 210 | 260 | 250 | 250 | |
Flexural Modulus | ISO 178 | GPa | 11.0 | 8.0 | 13.0 | 12.0 | 11.5 | |
Impact Strength | ISO 180 | kJ/m2 | 10.0 | 12.0 | 12.0 | 14.0 | 15.0 | |
Rockwell Hardness | ISO 2039/2 | R scale | 120 | 120 | 120 | 120 | 120 | |
Thermal | Heat Deflection Temperature | ISO 75 | °C | 265 | 265 | 265 | 265 | 265 |
Flammability Rating | UL-94 | - | V0 | V0 | V0 | V0 | V0 | |
Electrical | Volume Resistivity | ISO 167 | Ohm.cm | 5×1016 | 5×1016 | 5×1016 | 5×1016 | 5×1016 |
Dielectric Strength | ASTM D149 | KV/mm | 16 | 16 | 16 | 16 | 16 | |
Dielectric Constant | ASTM D150 | - | 3.6 | 3.6 | 3.8 | 3.8 | 3.8 | |
Wastage Factor | ASTM D150 | - | 0.002 | 0.002 | 0.002 | 0.002 | 0.002 | |
Process Conditions | Injection Temperature | - | °C | 290~330 | 290~330 | 290~330 | 290~330 | 290~330 |
Mold Temperature | - | °C | 120~150 | 120~150 | 120~150 | 120~150 | 120~150 | |
* MD: Mold direction; TD: Transverse direction | ||||||||